PC 8600E50 - Trinseo Recycled PCR USA
Price:70
Other Products
Description
Additional Information
EMERGE™ PC 8600E50-10 resin contains 50% post-consumer recycled (PCR) polycarbonate. This flame-retardant PC is free of chlorinated, brominated, or phosphate flame-retardant additives and complies with global environmental standards. The resin combines good mechanical, thermal, and chemical properties while maintaining excellent processability.
PC 8600E50- Trinseo Recycled PCR Applications
Electronics and Electrical Appliances
Charger and Adapter Housings
Information Technology Equipment
Basic Information
| Manufacturer Data | Material Datasheet (English) | |||
| Product Characteristics | Flame RetardantChlorine-FreeBromine-FreeRed Phosphorus-FreeEasy MoldingContains Recycled Material | |||
Technical Parameters
| Physical Properties | Value/Unit | Test Standard | Test Conditions |
|---|---|---|---|
Density | 1.2 g/cm³ | ASTM D792 | |
Melt Mass-Flow Rate (MFR) | |||
300°C/1.2 kg | 9 g/10min | ASTM D1238 | |
Shrinkage | |||
Flow Direction | 0.5~0.7 % | ASTM D 955 | |
| Mechanical Properties | Value/Unit | Test Standard | Test Conditions |
Tensile Strength | |||
Yield (yld) | 60 MPa | ASTM D638 | 50 mm/min |
Break (brk) | 65 MPa | ASTM D638 | 50 mm/min |
Tensile Elongation | |||
Yield (yld) | 6 % | ASTM D638 | 50 mm/min |
Break (brk) | 120 % | ASTM D638 | 50 mm/min |
Flexural Strength | |||
- | 95 MPa | ASTM D790 | 1.3 mm/min |
Flexural Modulus | 2400 MPa | ASTM D790 | 1.3 mm/min |
Tensile Modulus | 2300 MPa | ASTM D638 | 1.0 mm/min |
| Impact Properties | Value/Unit | Test Standard | Test Conditions |
Izod Notched Impact Strength | |||
23°C (73°F) | 750 J/m | ASTM D256 | |
| Thermal Properties | Value/Unit | Test Standard | Test Conditions |
Heat Deflection Temperature (HDT) | |||
1.8 MPa (264 psi) (18.6 kg/cm²) | 126 °C | ASTM D648 | Unannealed |
1.8 MPa (264 psi) (18.6 kg/cm²) | 125 °C | ISO 75-2/A | Unannealed |
Vicat Softening Temperature | 150 °C | ASTM D1525 | Rate B (120°C/h), Loading 1 (10 N) |
Vicat Softening Temperature | 150 °C | ISO 306/A120 | |
Coefficient of Linear Thermal Expansion (CLTE) | |||
Flow Direction | 65 E-6 cm/cm/°C | ASTM D 696 | -40 to 80°C |
Ball Pressure Test Temperature | 125 °C | IEC 60335-1 | |
Processing Temperature | 270~300 °C | - | |
Mold Temperature | 70~110 °C | - | |
| Flammability Properties | Value/Unit | Test Standard | Test Conditions |
UL Flame Rating | |||
HB | 0.4 mm | UL94 | |
V-2 | 0.55 mm | UL94 | |
V-1 | 1 mm | UL94 | |
V-0 | 1.5 mm | UL94 | |
V-0 | 2.5 mm | UL94 | |
V-0 | 3 mm | UL94 | |
Oxygen Index (LOI) | 35 % | ISO 4589 | |
Glow-Wire Flammability Index (GWFI) | |||
2mm | 960 °C | IEC 60695-2-12 | |
Glow-Wire Ignition Temperature (GWIT) | |||
2.0mm | 800 °C | IEC 60695-2-13 | |
| Electrical Properties | Value/Unit | Test Standard | Test Conditions |
Volume Resistivity | 1.0E+17 Ohm-cm | ASTM D257 | |
Dielectric Strength | 22 kV/mm | ASTM D149 | |
Arc Resistance | 7 PLC | ASTM D495 |